Product Description

Product Attributes

Model No.: XH-50N

Brand: xinghui

Place Of Origin: China

Classification: Double Components Adhesives

Main Ingredient: Polyurethane

Application Field: Packing

Resin System: polyester polyurethane polyol

Appearance: colorless or light yellow transparent viscous liquid

Viscosity(mPa.s 25℃): 1500-2500

Solid Content(%): 50±2

Solvent: ethyl acetate

Coating Amount(g/㎡): 2.5-5

Curing Temperature(℃): 40-50

Curing Time(h): 24-48

Packaging & Delivery

Selling Units	:	Kilogram
Package Type	:	20kg/barrel
Picture Example	:

The file is encrypted. Please fill in the following information to continue accessing it

Xinhui factory persentation vedio--specializing in research and production of polyurethane adhesives and resins for 26years



Product Description

XH-50N/K75 is a fast drying Two Component Solvent Based Polyurethane Adhesive. It is suitable for aluminum foil Myra, single-sided cable aluminum foil Myra, double-sided electric cable aluminum foil Myra and other aluminum foil Myra products. It is applied to the interlayer composite of composite materials such as PET and AL

Product characteristics

This Composite Adhesive has good adhesion to a variety of film substrates. It is a high transparency, high brightness, good film formation, fast curing, short curing time, tensile resistance Polyurethane Glue. With good initial adhesion, excellent peeling strength, and excellent flexibility of adhesive, Mylar film tensile test, the pinhole degree of aluminum film is small, mylar film is not easy to drop aluminum, product performance is stable. What is more, this adhesive for flexible packaging with good wetting, leveling performance, suitable for high and medium speed coating.

The coating amount of 2.5-5g/m²(dry base, according to the film structure after processing, use, quality requirements are different).

The temperature of the composite roller is generally controlled at 50℃-80℃, and the film susceptible to temperature is controlled at 50℃-60℃.

Dilution

Ethyl acetate is generally used; The water content of the solvent is required to be less than 0.2%, and it can not contain solvents containing active hydrogen such as alcohols and amines.